Gold Member Since 2016
Audited Supplier
Kunshan Chengweishang Special Steel Co., Ltd.

Die Steel Bar, Mould Steel, Cold Work Mould Steel manufacturer / supplier in China, offering High Quality 1.2379 Cold Work Mould Steel Round Bar, Steel Round Bar Cold Work Mould Steel 1.2510, Plastic Mould Steel 1.2311 Hot Rolled Steel Plate and so on.

(/ )

Supplier Homepage Product Cold work mould steel High Quality 1.2379 Cold Work Mould Steel Round Bar

High Quality 1.2379 Cold Work Mould Steel Round Bar

FOB Price: US $500-1,500 / Ton
Min. Order: 3 Tons
Min. Order FOB Price
3 Tons US $500-1,500/ Ton
Get Latest Price
Production Capacity: 1000 Tons/Month
Transport Package: Export Standard Packing or Customers′ Demand
Payment Terms: T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 1.2379/D2/SKD11/Cr12Mo1V1
  • Standard: AISI, GB, JIS, DIN
  • Technique: Forged
  • Surface Treatment: Black, Grinded, Rough Turned, Peeled, Polished
  • Special Use: Mold Steel
  • Delivery: 10-30 Days
  • Specification: 20-400)x(100-800)
  • HS Code: 7225
  • Type: Alloy Steel Bar
  • Steel Grade: 1.2379/D2/SKD11/Cr12Mo1V1
  • Application: Die Steel Bar
  • Alloy: Alloy
  • Payment: 30% Deposit,Blance by L/C at Sight or T/T
  • Trademark: CWS-Steel
  • Origin: China
Product Description
 
1.2379 Cold Work Mould Steel 
Introduction:
D2 is a high carbon - high chromium air hardening tool steel, heat treatable to 60-62 Rc. D2 offers excellent wear and abrasion resistance, due to large volumes of carbides in the microstructure. D2 is widely used in long production cold work applications requiring very high wear resistance and high compression strength. It is machinable in the annealed condition, and, like other air hardening tool steels, exhibits minimal distortion in heat treat. D2 is available in de-carb free rounds, flats, and squares, as well as ground flat stock and drill rod.
Applications include: 
 Typical applications for D2 tool steel are blanking, forming, and trim dies, gages, slitting cutters, wear parts, lamination dies, thread rolling dies, drawing dies, rotary cutting dies, knurls, bending dies, gages, shear blades, burnishing tools, rolls, machine parts, master parts, injection screw and tip components, seaming rolls, extrusion dies, tire shredders, scrap choppers, etc. 
Forging:
Heating for forging must be done slowly and uniformly. Soak through at 1850°-1950°F and reheat as often as necessary, stopping work when the temperature drops below 1700°F. After forging, cool slowly in lime, mica, dry ashes or furnace. D2 should always be annealed after forging. 
Annealing:
Heat slowly to 1550°-1600°F, hold until entire mass is heated through, and cool slowly in the furnace (40°F per hour) to about 1000°F, after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.  
Stress relieving: 
When desirable to relieve the strains of machining, heat slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving). 
Preheat prior to hardening:
Preheat slowly to 1350°-1450°F and hold at this temperature until material is uniformly heated. 
Hardening:
 After thorough preheating, heat to 1800°-1850°F. Hold the work piece at the hardening temperature until it is completely and uniformly heated. 
Quenching:
 D2 is an air hardening steel and will develop hardness on cooling in still air. To avoid scaling and prevent decarburization of the work piece surface, controlled atmosphere or vacuum furnaces are recommended. If these furnaces are not available, pack hardening, salt baths or wrapping the piece in stainless steel foil will provide some degree of surface protection in the hardening process. Parts should be allowed to cool to 150F, or to where they can be held in the bare hand, and then temper immediately. 
Tempering:
 The tempering temperature may be varied.
Equivalent gradesGBDINAISIJISBS
Cr12Mo1V11.2379D2SKD11BD2
Chemical CompositionCSiMnCrPSVMo Other   
1.50-1.600.10-0.40 0.15-0.4511.50-12.50 0.03MAX0.03MAX 0.90-1.10 0.60-0.80-
Available sizeRound BarDiameterLength
60-800mm2000-6000mm
Flat BarThicknessWidthLength
25-400mm200-800mm2000-6000mm
Surface conditionBlack surface/ Grinded/ Machined
Annealed hardnessHB225MAX
CharacteristicsVery high resistance against abrasive and adhesive wear due to a high volume of hard carbides in the steel matrix
moderate machinability, good dimensional stability,
toughness and through harden ability
ApplicationsShear blades,Thread rolling dies,Drawing and bending tools
Flanging and straightening rolls,Fine cutting tools
Deep drawing tools,Plastic mould for abrasive polymers
Cold extrusion dies,Drawing dies
Heat treatmentHardening
Harden from a temperature of 1000-1040oC followed by oil, warm bath (500-550oC, cooling bath or air. Hardness after quenching is 62-64 HRC.
Tempering
Tempering temperature: 150-550oC
Tempering Temperature (oC) vs. Hardness (HRC)
100°C200°C300°C400°C500°C
6361585859
Mechanical propertiesDensity7.7[g/cm3]
Thermal Conductivity        20.20 W/(m/k)
Specific heat capacity[J/g.K]0.46
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100°C20-200°C20-300°C20-400°C20-500°C
Send your message to this supplier
Avatar
Mr. Fortune Yang
Sales Manager
*From:
To: Mr. Fortune Yang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now